EPOKE SIL Silicone Mould Making 1:1 Ratio

 

EPOKE SIL Mould Making Silicone: when used as directed, is 0% shrinking and tear-resistant. Moulds manufactured with EPOKE SIL are durable and suitable for casting wax, gypsum, resins, concrete, and other materials.

Mixing Ratio: 1:1 by weight Eg: 10g Part A + 10g Part B

Pot Life: 30min @25 Degree Celsius

Cure time: 4-5Hours  @25 Degree Celsius

Temperature Resistance: Up to 200 Degree Celsius

Guidelines for use:

  • Measuring: Using a weighing scale measure Part A and Part B in a 1:1 ratio by weight (eg. 10g of Part A and 10g of Part B ) into a mixing container.
  • Mixing: Mix slowly and thoroughly making sure that you scrape the sides and bottom of the mixing container several times. Mix until mixture has attained a uniform colour without any unmixed streaks of material.
  • Pouring: For best results, pour your mixture in a single spot at the lowest point of the mould container. A uniform flow will help minimize entrapped air.  EPOKE SIL should level off at least 1/2” (1.3 cm) over the highest point of the model surface.
  • Curing: Allow EPOKE SIL silicone rubber to cure for 4-5 hours at room temperature (25°C) before de-moulding.

Mould Performance & Storage 

The physical life of the mould depends on how you use it (materials cast, frequency, etc.). Casting abrasive materials can quickly erode the mould detail while casting non-abrasive materials (wax) will not affect mould detail. Moulds should be stored on a level surface in a cool, dry environment.

 

 

 

Country of Origin: India

EPOKE SIL Silicone Mould Making 1:1 Ratio

Sale price Rs. 339.00
Regular price Rs. 399.00You saved 15% OFF

Tax included. Shipping calculated at checkout

Exclusive Offers
  • Get an Additional 5% OFF on Purchases of ₹2499 & above use code ADD5
  • Get an Additional 5% OFF no minimum order value. Use code NEW5 for First Time users only
  • 100gm (50gm - PART A/B)
  • 500gm (250gm - PART A/B)

Description

EPOKE SIL Silicone Mould Making 1:1 Ratio

 

EPOKE SIL Mould Making Silicone: when used as directed, is 0% shrinking and tear-resistant. Moulds manufactured with EPOKE SIL are durable and suitable for casting wax, gypsum, resins, concrete, and other materials.

Mixing Ratio: 1:1 by weight Eg: 10g Part A + 10g Part B

Pot Life: 30min @25 Degree Celsius

Cure time: 4-5Hours  @25 Degree Celsius

Temperature Resistance: Up to 200 Degree Celsius

Guidelines for use:

  • Measuring: Using a weighing scale measure Part A and Part B in a 1:1 ratio by weight (eg. 10g of Part A and 10g of Part B ) into a mixing container.
  • Mixing: Mix slowly and thoroughly making sure that you scrape the sides and bottom of the mixing container several times. Mix until mixture has attained a uniform colour without any unmixed streaks of material.
  • Pouring: For best results, pour your mixture in a single spot at the lowest point of the mould container. A uniform flow will help minimize entrapped air.  EPOKE SIL should level off at least 1/2” (1.3 cm) over the highest point of the model surface.
  • Curing: Allow EPOKE SIL silicone rubber to cure for 4-5 hours at room temperature (25°C) before de-moulding.

Mould Performance & Storage 

The physical life of the mould depends on how you use it (materials cast, frequency, etc.). Casting abrasive materials can quickly erode the mould detail while casting non-abrasive materials (wax) will not affect mould detail. Moulds should be stored on a level surface in a cool, dry environment.

 

 

 

Country of Origin: India